Hot Dipped Galvanized Binding Wire is made of high quality bright annealed steel wire supplied in big coils for tying tools.
Processing
The steel wire is drawn, annealed, hot dipped zinc coated, winding into various binding wire forms.
Finished Forms: Big coils.
Major Products
Hot Dipped Galvanized Steel Binding Wires 0.90mm, 1.25mm, 1.60mm, 2.00mm, 2.50mm, 3.05mm
Wire Diameter and Zinc Coating Quantity:
HDG Binding Wire 0.90 mm, zinc coating min. 130 g/m2
HDG Binding Wire 1.25 mm, zinc coating min. 170 g/m2
HDG Binding Wire 1.60 mm, zinc coating min. 195 g/m2
HDG Binding Wire 2.00 mm, zinc coating min. 210 g/m2
HDG Binding Wire 2.50 mm, zinc coating min. 215 g/m2
HDG Binding Wire 3.05 mm, zinc coating min. 225 g/m2
Technical Requirements:
Tensile Strength : 340 - 500 N/mm²
Wrapping test : Wrapping test around a mandrel for one complete turn. The mandrel shall have a diameter of 4d (d nominal wire diameter)- wires shall not break
Elongation : 10% for all size, with exception of 0.87mm wire which should have minimum elongation at break of 7.5%.
Resistivity: Max resistivity 138 Ohm.mm2/km at 20 0C.
Packing: In big coils.
Coil diameter, Inner Diameter: 340-500 mm
Outer Diameter: 850-900 mm
Coil Weight: 550 - 650 KGS